This study focuses to provide information about reinforcing influences of nanoparticles exerted on the mechanical and fracture mechanical properties of epoxy resins, particularly with regard to fracture and toughening mechanisms. A comprehensive study was carried out on series of nanocomposites containing varying amounts of nanoparticles, either titanium dioxide (TiO2) or aluminium oxide (Al2O3). Nanocomposites were systematically produced by applying high (shear) energy during a controlled d...This study focuses to provide information about reinforcing influences of nanoparticles exerted on the mechanical and fracture mechanical properties of epoxy resins, particularly with regard to fracture and toughening mechanisms. A comprehensive study was carried out on series of nanocomposites containing varying amounts of nanoparticles, either titanium dioxide (TiO2) or aluminium oxide (Al2O3). Nanocomposites were systematically produced by applying high (shear) energy during a controlled dispersion process, in order to reduce the size of agglomerates and to gain a homogeneous distribution of individual nanoparticles within the epoxy resin. The mechanical performance of the nanocomposites was then characterized by flexural testing, dynamic mechanical analysis (DMA), and furthermore, by fracture mechanics approaches (LEFM) and fatigue crack growth testing (FCP). The microstructure of specimens and the corresponding fracture surfaces were examined by TEM, SEM and AFM techniques in order to identify the relevant fracture mechanisms involved, and to gain information about the dispersion quality of nanoparticles within the polymer. It was found that the presence of nanoparticles in epoxy induces various fracture mechanisms, e.g. crack deflection, plastic deformation, and crack pinning. At the same time, nanoparticles can overcome the drawbacks of traditional tougheners (e.g. glass beads or rubber particles) by simultaneously improving stiffness, strength and toughness of epoxy, without sacrificing thermo-mechanical properties.» weiterlesen» einklappen

Autoren

Klassifikation

DDC Sachgruppe:
Ingenieurwissenschaften