Inhaltszusammenfassung

The understanding of the coupling between superconducting YBa2Cu3O7 (YBCO) layers decoupled by non superconducting PrBa2Cu3O7 (PBCO) layers in c-axis oriented superlattices was the aim of this thesis. For this purpose two conceptually different kind of transport experiments have been performed. rnrnIn the first type of transport experiments the current is flowing parallel to the layers. Here the coupling is probed indirectly using magnetic vortex lines, which are penetrating the superlattice...The understanding of the coupling between superconducting YBa2Cu3O7 (YBCO) layers decoupled by non superconducting PrBa2Cu3O7 (PBCO) layers in c-axis oriented superlattices was the aim of this thesis. For this purpose two conceptually different kind of transport experiments have been performed. rnrnIn the first type of transport experiments the current is flowing parallel to the layers. Here the coupling is probed indirectly using magnetic vortex lines, which are penetrating the superlattice. Movement of the vortex segments in neighbouring YBCO layers is more or less coherent depending on the thickness of both the superconducting and non superconducting layers. This in-plane transport was measured either by sending an external current through bridges patterned in the superlattice or by an induced internal current. rnThe vortex-creep activation energy U was determined by analysis of the in-plane resistive transition in an external magnetic field B oriented along the c-axis. The activation energies for two series of superlattices were investigated. In one series the thickness of the YBCO layers was constant (nY=4 unit cells) and the number of the PBCO unit cells was varied, while in the other the number of PBCO layers was constant (nP=4) and nY varied. The correlation length of the vortex system was determined to be 80 nm along the c-axis direction. It was found that even a single PBCO unit cell in a superlattice effectively cuts the flux lines into shorter weakly coupled segments, and the coupling of the vortex systems in neighbouring layers is negligible already for a thickness of four unit cells of the PBCO layers. A characteristic variation of the activation energy for the two series of superlattices was found, where U0 is proportional to the YBCO thickness. A change in the variation of U0 with the current I in the specimen was observed, which can be explained in terms of a crossover in the vortex creep process, generated by the transport current. At low I values the dislocations mediated (plastic) vortex creep leads to thermally assisted flux-flow behaviour, whereas at high current the dc transport measurements are dominated by elastic (collective) creep.rnThe analysis of standard dc magnetization relaxation data obtained for a series superlattices revealed the occurrence of a crossover from elastic (collective) vortex creep at low temperature to plastic vortex creep at high T. The crossover is generated by the T dependent macroscopic currents induced in the sample. The existence of this creep crossover suggests that, compared with the well known Maley technique, the use of the normalized vortex creep activation energy is a better solution for the determination of vortex creep parameters.rnrnThe second type of transport experiments was to measure directly a possible Josephson coupling between superconducting CuO2 double planes in the superlattices by investigation of the transport properties perpendicular to the superconducting planes. Here three different experiments have been performed. The first one was to pattern mesa structures photolithographically as in previous works. The second used three-dimensional nanostructures cut by a focused ion beam. For the these two experiments insufficient patterning capabilities prevented an observation of the Josephson effect in the current voltage curves. rnA third experiment used a-axis and (110) oriented YBCO films, where in-plane patterning can in principle be sufficient to measure transport perpendicular to the superconducting planes. Therefore the deposition of films with this unusual growth orientation was optimized and investigated. The structural and microstructural evolution of c-axis to a-axis orientation was monitored using x-ray diffraction, scanning electron microscopy and magnetization measurements. Films with full a-axis alignment parallel to the substrate normal could be achieved on (100)SrTiO3. Due to the symmetry of the substrate the c-axis direction in-plane is twofold. Transferring the deposition conditions to films grown on (110)SrTiO3 allowed the growth of (110) oriented YBCO films with a unique in-plane c-axis orientation. While these films were of high quality by crystallographic and macroscopic visual inspection, electron microscopy revealed a coherent crack pattern on a nanoscale. Therefore the actual current path in the sample was not determined by the macroscopic patterning which prohibited investigations of the in-plane anisotropy in this case.rn» weiterlesen» einklappen

Autoren

Klassifikation

DDC Sachgruppe:
Physik