Inhaltszusammenfassung

Heusler compounds as thermoelectric materialsrnrnThis work reports on Heusler and Half Heusler compounds and their thermoelectric properties. Several compounds were synthesized and their resistivity, Seebeck coefficient, thermal conductivity, and the figure of merit were determined. The results are presented in the following chapters.rnrnIn chapter 3 Co was substituted with Ni and Fe in the series TiCo1-x(Fe0.5Ni0.5)xSb. The substitution lead to a reduced loss of Sb during the synthesis. Furt...Heusler compounds as thermoelectric materialsrnrnThis work reports on Heusler and Half Heusler compounds and their thermoelectric properties. Several compounds were synthesized and their resistivity, Seebeck coefficient, thermal conductivity, and the figure of merit were determined. The results are presented in the following chapters.rnrnIn chapter 3 Co was substituted with Ni and Fe in the series TiCo1-x(Fe0.5Ni0.5)xSb. The substitution lead to a reduced loss of Sb during the synthesis. Further the Seebeck coefficient was increased and the thermal conductivity was reduced. These observations can be used to significantly improve the quality of TiCoSb based compounds in thermoelectric applications. rnrnIn chapter 4 the series TiCo1-xNixSnxSb1-x was investigated. Ni was substituted with Co and Sn with Sb. Especially for high Ni concentrations the figure of merit was enhanced compared to unsubstituted TiCoSb. This enhancement is based on the strong reduction of the thermal conductivity. The found values are among the lowest that have been determined up to date for Heusler compounds. rnrnIn chapter 5 Li containing Heusler compounds were theoretically and experimentally investigated. Li containing Heusler compounds are of special interest because the Li atoms scatter phonons efficiently. Therefore the thermal conductivity is decreased. The thermoelectric properties and especially the thermal conductivity are investigated in this chapter.rnrnIn chapter 6 several substitutions of TiCoSb were investigated. In the series TiCo1+xSb additional Co was introduced into the vacancies of the compound and the effect on the thermoelectric properties was measured. In the series TiCo1-xCuxSb Co was substituted with Cu. No significant enhancement of the ZT value were observed. In the series TiCoSb1-xBix Sb was substituted by Bi. The thermoelectric properties were significantly enhanced for small Bi concentrations. The Seebeck coefficient was increased and the resistivity was reduced at the same time. This unusual phenomenon is explained by band structure calculations.rnrnIn chapter 7 the material class of half metallic ferromagnets was investigated as a new materialclass for thermoelectric applications. The 26 valence electron compounds Co2TiSi, Co2TiGe, and Co2TiSn were used as model systems. The transport properties were determined theoretically. Then the properties were measured and compared to the calculated ones. The calculated values are in good agreement with the experimentally determined ones. The observed Seebeck coefficient has a big value and is nearly constant above the Curie temperature. This makes the materials appealing for the use as materials in thermocouples.rn» weiterlesen» einklappen

Autoren

Klassifikation

DDC Sachgruppe:
Chemie