Due to its high Curie temperature of 420K and band structure calculations predicting 100% spin polarisation, Sr2FeMoO6 is a potential candidate for spintronic devices. However, the preparation of good quality thin films has proven to be a non-trivial task. Epitaxial Sr2FeMoO6 thin films were prepared by pulsed laser deposition on different substrates. Differing from previous reports a post-deposition annealing step at low oxygen partial pressure (10-5 mbar) was introduced and enabled the fab...Due to its high Curie temperature of 420K and band structure calculations predicting 100% spin polarisation, Sr2FeMoO6 is a potential candidate for spintronic devices. However, the preparation of good quality thin films has proven to be a non-trivial task. Epitaxial Sr2FeMoO6 thin films were prepared by pulsed laser deposition on different substrates. Differing from previous reports a post-deposition annealing step at low oxygen partial pressure (10-5 mbar) was introduced and enabled the fabrication of reproducible, high quality samples. According to the structural properties of the substrates the crystal structure and morphology of the thin films are modified. The close interrelation between the structural, magnetic and electronic properties of Sr2FeMoO6 was studied. A detailed evaluation of the results allowed to extract valuable information on the microscopic nature of magnetism and charge transport. Smooth films with a mean roughness of about 2 nm have been achieved, which is a pre-requisite for a possible inclusion of this material in future devices. In order to establish device-oriented sub-micron patterning as a standard technique, electron beam lithography and focussed ion beam etching facilities have been put into operation. A detailed characterisation of these systems has been performed. To determine the technological prospects of new spintronics materials, the verification of a high spin polarisation is of vital interest. A popular technique for this task is point contact Andreev reflection (PCAR). Commonly, the charge transport in a transparent metal-superconductor contact of nanometer dimensions is attributed solely to coherent transport. If this condition is not fulfilled, inelastic processes in the constriction have to be considered. PCAR has been applied to Sr2FeMoO6 and the Heusler compound Co2Cr0.6Fe0.4Al. Systematic deviations between measured spectra and the standard models of PCAR have been observed. Therefore existing approaches have been generalised, in order to include the influence of heating. With the extended model the measured data was successfully reproduced but the analysis has revealed grave implications for the determination of spin polarisation, which was found to break down completely in certain cases.» weiterlesen» einklappen

Autoren

Klassifikation

DDC Sachgruppe:
Physik