Vortex dynamics in two different classes of superconductors with anisotropic unidirected pinning sites was experimentally investigated by magnetoresistivity measurements: YBCO−films with unidirected twins and Nb-films deposited on faceted $mathrm Al_2O_3$ substrate surfaces. For the interpretation of the experimental results a theoretical model based on the Fokker-Planck equation was used. It was proved by X-ray measurements that YBCO films prepared on (001) $mathrm NdGaO_3$ substrates...Vortex dynamics in two different classes of superconductors with anisotropic unidirected pinning sites was experimentally investigated by magnetoresistivity measurements: YBCO−films with unidirected twins and Nb-films deposited on faceted $mathrm Al_2O_3$ substrate surfaces. For the interpretation of the experimental results a theoretical model based on the Fokker-Planck equation was used. It was proved by X-ray measurements that YBCO films prepared on (001) $mathrm NdGaO_3$ substrates exhibit only one twin orientation in contrast to YBCO films grown on (100) $mathrm SrTiO_$3 substrates. The magnetoresistivity measurements of the YBCO films with unidirected twin boundaries revealed the existence of two new magnetoresistivity components, which is a characteristic feature of a guided vortex motion: an odd longitudinal component with respect to the magnetic field sign reversal and an even transversal component. However, due to the small coherence length in YBCO and the higher density of point-like defects comparing to high-quality YBCO single crystals, the strength of the isotropic point pinning was comparable with the strength of the pinning produced by twins. This smeared out all effects caused by the pinning anisotropy. The behaviour of the odd longitudinal component was found to be independent of the transport current direction with respect to the twin planes. The magnetoresistivity measurements of faceted Nb films demonstrated the appearance of an odd longitudinal and even transversal component of the magnetoresistivity. The temperature and magnetic field dependences of all relevant magnetoresistivity components were measured. The angles between the average vortex velocity vector and the transport current direction calculated from the experimental data for the different transport current orientations with respect to the facet ridges showed that the vortices moved indeed along the facet ridges. An anomalous Hall effect, i.e. a sign change of the odd transversal magnetoresistivity, has been found in the temperature and magnetic field dependences of the Hall resisitivity of the samples. The theory developed by V.~A.~Shklovskij was used for the explanation of the experimental data. It shows very good agreement with the experiment. The temperature dependence of the even longitudinal magnetoresistivity component of the samples could be very well fitted within the theoretical approach, using for the isotropic and anisotropic pinning potential simple potential with a symmetric triangular potential wells whose depths were estimated from the experimental data.» weiterlesen» einklappen

Autoren

Klassifikation

DDC Sachgruppe:
Physik