Improvement in carrier mobility and photovoltaic performance through random distribution of segments of linear and branched side chains

Journal of materials chemistry : an interdisciplinary journal covering all aspects of materials chemistry. Bd. 20. H. 43. Cambridge: Royal Soc. of Chemistry 2010 S. 9726 - 9734

Erscheinungsjahr: 2010

ISBN/ISSN: 0959-9428

Publikationstyp: Zeitschriftenaufsatz

Sprache: Englisch

Doi/URN: 10.1039/c0jm01482f

Volltext über DOI/URN

GeprüftBibliothek

Inhaltszusammenfassung


The random distribution of segments of linear octyloxy side chains and of branched 2-ethylhexyloxy side chains, on the backbone of anthracene containing poly(p-phenylene-ethynylene)-alt-poly-(p-phenylene-vinylene) (PPE-PPV) has resulted in a side chain based statistical copolymer, denoted AnE-PVstat, showing optimized features as compared to the well defined homologues whose constitutional units are incorporated into its backbone. Electric field independent charge carrier mobility (mu(hole)) ...The random distribution of segments of linear octyloxy side chains and of branched 2-ethylhexyloxy side chains, on the backbone of anthracene containing poly(p-phenylene-ethynylene)-alt-poly-(p-phenylene-vinylene) (PPE-PPV) has resulted in a side chain based statistical copolymer, denoted AnE-PVstat, showing optimized features as compared to the well defined homologues whose constitutional units are incorporated into its backbone. Electric field independent charge carrier mobility (mu(hole)) for AnE-PVstat was demonstrated by CELIV and OFET measurements, both methods resulting in similar mhole values of up to 5.43 x 10(-4) cm(2) V(-1) s(-1). Upon comparison, our results show that charge carrier mobility as measured by CELIV technique is predominantly an intrachain process and less an interchain one, which is in line with past photoconductivity results from PPE-PPV based materials. The present side chain distribution favors efficient solar cell active layer phase separation. As a result, a smaller amount of PC(60)BM is needed to achieve relatively high energy conversion efficiencies above 3%. The efficiency of eta(AM1.5) approximate to 3.8% obtained for AnE-PVstat:PC(60)BM blend is presently the state-of-art value for PPV-based materials.» weiterlesen» einklappen

Autoren


Egbe, Daniel A. M. (Autor)
Adam, Getachew (Autor)
Pivrikas, Almantas (Autor)
Ramil, Alberto M. (Autor)
Birckner, Eckhard (Autor)
Cimrova, Vera (Autor)
Hoppe, Harald (Autor)
Sariciftci, Niyazi Serdar (Autor)

Klassifikation


DDC Sachgruppe:
Chemie

Verknüpfte Personen