The dried blends containing sodium and ammonium salts of lignite humic acids (humates, 0.5-10% w/w) in polyvinyl alcohol (PVA) were exposed to high dosage of gamma-irradiation in the range of doses 127-806 kGy. Resulted products were then tested for their stability using thermogravimetrical analysis. As a reference the non-treated blends were used since the pure PVA exposed to gamma-irradiation very quickly lost its stability and resulting consistence did not allow the stability tests. Stabil...The dried blends containing sodium and ammonium salts of lignite humic acids (humates, 0.5-10% w/w) in polyvinyl alcohol (PVA) were exposed to high dosage of gamma-irradiation in the range of doses 127-806 kGy. Resulted products were then tested for their stability using thermogravimetrical analysis. As a reference the non-treated blends were used since the pure PVA exposed to gamma-irradiation very quickly lost its stability and resulting consistence did not allow the stability tests. Stabilities showed a strong concentration and counterion dependency. While sodium counterion caused mostly destabilization with increasing dose, the ammonium counterion acted in an opposite way. The tests carried out in a moisturizing container revealed the changes in water absorbing capacity of irradiated samples and allowed partial explanation of humate stabilizing effect. Generally, at lower concentration of a humate the increase was observed with an increase in the gamma-irradiation dose and vice versa. The results confirmed the antioxidant and stabilizing effect of humic acids added to some synthetic polymers and their applicability in materials exposed to gamma-irradiation. » weiterlesen» einklappen

Autoren