Inhaltszusammenfassung

Infrared reflectivity of an oxygen reduced YBa2Cu3O6.7 thin film was measured in the frequency range 30 cm-1 < v < 7000 cm-1 and for temperatures 5 K < T < 300 K. At lower frequencies, 3 cm-1 < v < 40 cm-1, the complex conductivity *=1+i2 was measured directly using a transmission technique. Both data sets were combined to obtain the reflectivity in a broad frequency range and thus to improve substantially the quality of the Kramers-Kronig analysis at low frequencies. The analysis of the cond...Infrared reflectivity of an oxygen reduced YBa2Cu3O6.7 thin film was measured in the frequency range 30 cm-1 < v < 7000 cm-1 and for temperatures 5 K < T < 300 K. At lower frequencies, 3 cm-1 < v < 40 cm-1, the complex conductivity *=1+i2 was measured directly using a transmission technique. Both data sets were combined to obtain the reflectivity in a broad frequency range and thus to improve substantially the quality of the Kramers-Kronig analysis at low frequencies. The analysis of the conductivity spectra reveals that the low-frequency spectral weight strongly depends on temperature directly above TC but saturates for T ≥ 150 K. » weiterlesen» einklappen

Autoren

Klassifikation

DFG Fachgebiet:
Physik der kondensierten Materie

DDC Sachgruppe:
Physik