The relaxation of the irreversible magnetization of MgB2 bulk samples obtained by electric-field assisted sintering was investigated using the SQUID magnetometry for a magnetic field H up to 50 kOe applied in zero-field-cooling conditions. We observed a crossover plastic creep at high temperatures T-elastic creep at low T, described by H ? T?2 in the low T range, which appears to be caused by the macroscopic currents induced in the sample during magnetization measurements. By decreasing T bel...The relaxation of the irreversible magnetization of MgB2 bulk samples obtained by electric-field assisted sintering was investigated using the SQUID magnetometry for a magnetic field H up to 50 kOe applied in zero-field-cooling conditions. We observed a crossover plastic creep at high temperatures T-elastic creep at low T, described by H ? T?2 in the low T range, which appears to be caused by the macroscopic currents induced in the sample during magnetization measurements. By decreasing T below this line the determined creep exponent rapidly overcomes the widely accepted theoretical values for elastic (collective) pinning. This behaviour can easily be explained through the occurrence of micro flux jumps, leading to a finite magnetization relaxation rate in the low-T limit. » weiterlesen» einklappen

Autoren

Klassifikation

DFG Fachgebiet:
Physik der kondensierten Materie

DDC Sachgruppe:
Physik