We experimentally establish a phase diagram of thin films of concentrated solutions of a cylinder forming polystyrene-block-polybutadiene-block-polystyrene triblock copolymer in chloroform. During annealing the film forms islands and holes with energetically favored values of film thickness. The thin film structure depends on the local thickness of the film and the polymer concentration. Typically, at a thickness close to a favored film thickness parallel orientation of cylinders is observed,...We experimentally establish a phase diagram of thin films of concentrated solutions of a cylinder forming polystyrene-block-polybutadiene-block-polystyrene triblock copolymer in chloroform. During annealing the film forms islands and holes with energetically favored values of film thickness. The thin film structure depends on the local thickness of the film and the polymer concentration. Typically, at a thickness close to a favored film thickness parallel orientation of cylinders is observed, while perpendicular orientation is formed at an intermediate film thickness. At high polymer concentration the cylindrical microdomains reconstruct to a perforated lamella structure. Deviations from the bulk structure, such as the perforated lamella and a wetting layer are stabilized in films thinner than approximate to1.5 domain spacings. (C) 2004 American Institute of Physics.» weiterlesen» einklappen

Autoren

Klassifikation

DDC Sachgruppe:
Physik