Inhaltszusammenfassung

The effects of current induced Néel spin-orbit torques on the antiferromagnetic domain structure of epitaxial Mn2Au thin films were investigated by x-ray magnetic linear dichroism–photoemission electron microscopy. We observed current induced switching of antiferromagnetic domains essentially corresponding to morphological features of the samples. Reversible as well as irreversible Néel vector reorientation was obtained in different parts of the samples and the switching of up to 30% of all d...The effects of current induced Néel spin-orbit torques on the antiferromagnetic domain structure of epitaxial Mn2Au thin films were investigated by x-ray magnetic linear dichroism–photoemission electron microscopy. We observed current induced switching of antiferromagnetic domains essentially corresponding to morphological features of the samples. Reversible as well as irreversible Néel vector reorientation was obtained in different parts of the samples and the switching of up to 30% of all domains in the field of view of 10 μm is demonstrated. Our direct microscopical observations are compared to and fully consistent with anisotropic magnetoresistance effects previously attributed to current induced Néel vector switching in Mn2Au.» weiterlesen» einklappen

Autoren

Klassifikation

DDC Sachgruppe:
Physik